Cutting Edge 1045 Cold Rolled Steel Plate
- Wechat:18365798883
- WhatsApp:+86-18365798883
- E-Mali:admin@sdxyy.cn
1045 Cold Rolled Steel Plate
Carbon steels are a category of steels containing 0.12 to 2% carbon. AISI 1045 is a medium carbon steel specifically engineered to provide enhanced strength and hardness. This steel exhibits exceptional size accuracy, concentricity, and straightness, which collectively help reduce wear in high-speed applications. AISI 1045 can be shaped into turned, ground, and polished bars that can be machined asymmetrically with minimal distortion.
The subsequent sections will provide a detailed discussion of AISI 1045 carbon steel.
Product Parameters
| Product Name | 1045 Cold Rolled Steel Plate |
| Type | Hot Rolling, Cold Rolling |
| Thickness | 0.1mm-400mm |
| Length | 1m-12m, or Customized Size |
| Width | 100mm-3000mm |
| Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc. |
| Surface | BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. |
| Scope of Application | The following are the application areas of AISI 1045 carbon steel: ● Bolts ● Studs ● Gears ● Axles ● Shafts ● Machine parts. |
| Certificate | ISO, SGS, BV, etc. |
| Production Technology | Rolling, Annealing, Quenching, Tempered or Standard |
| Edge Processing | Ordinary, Wire Drawing, Laminated Film |
Chemical Composition
|
Element |
Content (%) |
|
Carbon, C |
0.43-0.50 |
|
Manganese, Mn |
0.60-0.90 |
|
Sulfur, S |
0.05 (max) |
|
Phosphorous, P |
0.04 (max) |
|
Iron, Fe |
Balance |
Mechanical Properties
|
Properties |
Metric |
Imperial |
|
Tensile strength |
585 MPa |
84800 psi |
|
Yield strength |
450 MPa |
65300 psi |
|
Modulus of elasticity |
200 GPa |
29000 ksi |
|
Shear modulus (typical for steel) |
80 GPa |
11600 ksi |
|
Poisson’s ratio |
0.29 |
0.29 |
|
Elongation at break (in 50 mm) |
12 % |
12 % |
|
Hardness, Brinell |
163 |
163 |
|
Hardness, Knoop (converted from Brinell hardness) |
184 |
184 |
|
Hardness, Rockwell B (converted from Brinell hardness) |
84 |
84 |
|
Hardness, Vickers (converted from Brinell hardness) |
170 |
170 |