High Strength 316Ti Stainless Steel Bar
- Wechat:18365798883
- WhatsApp:+86-18365798883
- E-Mali:admin@sdxyy.cn
316Ti Stainless Steel Bar Description
316Ti stainless steel bars are highly resistant to various corrosive media, including acids, alkalis, and salts, due to their high chromium and nickel content. The addition of titanium enhances corrosion resistance by creating a stable passivation film. These bars exhibit excellent processing properties, including weldability, bending formability, and machining performance, facilitating efficient manufacturing processes. Furthermore, 316Ti stainless steel bars can be utilized in a temperature range of -253°C to 400°C without compromising strength and stability, making them suitable for use in high-temperature environments as manufacturing parts.
Product Parameters
| Product Name | High Strength 316Ti Stainless Steel Bar | |
| Type | Steel Bar | |
| Outer Diameter | Round Bar | 4mm-500mm |
| Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
| Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
| Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
| Length | 1-6 meters, Length can be customized | |
| Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
| Surface | Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. | |
| Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc. | |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P | Mo | Ti |
| ≤ 0.08 | ≤1.0 | ≤ 2.0 | 16.0～18.0 | 10.0～14.0 | ≤ 0.03 | ≤ 0.045 | 2.0～3.0 | 0.5～0.7 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥515 | ≥205 | ≥ 40 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
| 7.99 | 193 | 16.0 | 16.2 | 74 |