Premium Grade 410 Stainless Steel Plate
- Wechat:18365798883
- WhatsApp:+86-18365798883
- E-Mali:admin@sdxyy.cn
410 Stainless Steel Plate Description
410 stainless steel is a type of martensitic stainless steel with a chromium content of 11.5% and exceptional corrosion resistance. It has undergone quenching, tempering, and polishing processes to enhance its corrosion resistance and hardness. Compared to austenitic stainless steel, martensitic stainless steel is relatively inferior, necessitating a final heat treatment during manufacturing. Grade 410 stainless steel demonstrates the ability to withstand hot gases, steam, food, weak acids and bases, fresh water, and dry air. This steel is hardened to maximize corrosion and heat resistance. Widely used in automotive manufacturing, 410 stainless steel is valued for its high strength, making it well-suited for applications requiring durability and wear resistance.
Product Parameters
| Product Name | 410 Stainless Steel Plate |
| Type | Plate |
| Thickness | 0.3mm-200mm |
| Length | 2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc. |
| Width | 40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc. |
| Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. |
| Surface | BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. |
| Scope of Application | This stainless steel finds widespread application across various industries, including high-temperature and electrical sectors, medical equipment construction, chemical and food industries, agriculture, ship parts, food and beverage packaging, kitchen supplies, trains, airplanes, conveyor belts, vehicles, as well as in bolts, nuts, springs, and screens, among others. |
| Certificate | ISO, SGS, BV, etc. |
| Production Technology | Hot Rolling, Cold Rolling |
| Edge Processing | Edging, Trimming |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P |
| ≤ 0.15 | ≤1.0 | ≤1.0 | 11.5～13.5 | ≤ 0.5 | ≤ 0.03 | ≤ 0.04 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥450 | ≥205 | ≥20 | ≤ 201HB |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
| 7.74 | 200 | 9.9 | 24.9 | 570 |
Surface Selection